The Genesis of a Lord of Change

Post by Korto »

I'm thinking about starting a small 40K Tzeentch daemon force, but given my small budget, and long list of more important things to spend on, I figured I might just have a go at making them myself. Hey, how hard can it be if a pack of Poms can manage it, right? :)
And so this records the creation of my Lord of Change, using the Lost Wax process of casting.

First thing I realised is that I didn't have to try and copy GW. This is Chaos, right? And Tzeentch, the Changer of the Ways at that. They would look like all kinds of different shit, some scary, some sad, some cute, some just plain weird. I'd be best served keeping everything I make unique.
Unique. Original. Every single figure. Ummm... shit.

So I start by just working some wax into shapes while thinking, and then I start thinking... eyestalks.
Image
The wax I'm using here is a custom blend of bee's wax and, ummm, something else (might be petroleum jelly. The wax bloke told me, but I forget) at a ratio to create a wax that is carveable at room temperature but mouldable at body temperature. It's also sticky enough to accept having extra bits of wax added and merged in easily.

Image
The creature starts taking shape. I'm sticking it on a base here to make sure it fits. A fantasy base, since that's what I have handy.

Image
The finished wax. I'm trying an idea here where the staff is in three pieces, but still floating in place as if it is whole, just hovering there in space. As "hovering in space" is a difficult trick for metal to do in the real world, each piece is in fact connected to the figure. The centre is of course held in its hand, while the top piece brushes against an eyestalk, and the bottom 'happens' to rest against his leg.
Behind the Lord of Change, you can see a Verminlord that I was using as a size comparison while I was making the figure.

Image
Next, he has to be connected to a tree. You see here the Lord of Change surrounded by other daemons of various types. The trunk of the tree is aluminium, short wax in-gates attach the figures to the trunk, and drips of molten wax are used to solid the join (don't skimp on the molten wax. Something coming loose later is a major, and often irretrievable, disaster)
The important thing to know about this tree when understanding how it works, is that it is, in a very real sense, upside down.

Upside down, upside down, Miss Jane!

Image
Looking at it this way, the metal pours into the top, and the mushrooming out at the top creates a handy pouring cup. The metal runs down the stalk, through the in-gates, and into the figures.
Near the top, you can see thin wax lines running from the figures. They're called whistlers, and allow air to escape. They're attached to every significant high point where air could be trapped, and can sometimes be a bit of a delicate bugger to attach.
As you can see, there's a fair amount of figures, stuck all around in any way they can fit, and the whole thing is rather complex. This is to get the most figures for the least amount of time and material, although there are drawbacks to doing this. (More on that later)
Notice the gap between the top of the stalk and the top of the figures, which is a bit of an odd thing considering I've just intimated I'm trying to get the most out for the least cost. The reason for this is two-fold. Firstly, the extra height provides more pressure from weight of metal to push the metal into the figures, and secondly, and more importantly, to try to prevent shrinkage. As the metal hardens, it shrinks, and when it shrinks it draws in molten metal to fill the void, and it firstly tries to get it from above (letting gravity do the work). This means the metal level in the pourer spout will drop from the level you fill it to, sometimes quite precipitously (depending upon the shape of your job). If the level falls below the level of your job, you will likely get shrinkage in your job. Throw it away, try again.

Shrinkage is something you always have to keep in mind when casting. The metal will shrink. It will try to draw in more metal. Where will it draw it from? If you don't give it an easy source, it'll create one of its own.
Also, only liquid metal shrinks (OK, all metal expands and contracts, solid, liquid or gas, but for this foundry usage of the word "shrinkage", OK?), and mostly when hardening, and it only draws from liquid metal. This means a few things, some you can take advantage of, and some you have to look out for. For instance, a thin spindly job attached to a thick chunky pourer will freeze off well before the pourer, meaning the job will be able to draw from the pourer till it freezes off, and then the pourer can't draw from the job (this is partly what I'm doing). If you reversed that, having a thin pourer into a thick job, the pourer would freeze first (drawing from you job), and then your job would be isolated and would cannibalise itself.
A thick pourer is a bugger to cut off, and so you may want a thin connector between the two (the connection between the pourer and the job is called an "in-gate"), which is easier to cut. However, if that thin connector should freeze before the job, then your job may be cut off from its metal supply, and it will cannibalise itself. This can often be avoided by making the in-gate short enough so that the nearby heat of the pourer keeps it molten. You hope.
If it's a big job, and the pourer is too far away, then all the best intentions in the world wont stop shrinkage in the far reaches. In this case, you can use "risers", which are extra shafts, similar to the pourer, connected to your job. The metal rises up in them from your job while you're pouring, and you continue pouring until all risers are full (if they don't fill properly, you can also pour metal down into them, and pray). Then while your job freezes off, it can also draw from the risers; they also help prevent air from being trapped. A teacher once told me that as a rule of thumb, a riser protects a radius equal to twice the riser's diametre.

Anyway.

Image
Weighing the completed tree. As you can see, only the latest high-tech gear for us!
As I already know the weight of the aluminium stalk, this step tells me how much wax is in the thing (and it's a step I regularly forget. Oh well.)
With a weight of 462g, but the stalk is 350g, that leaves 112g of wax. Must write that down somewhere, or I'll forget.

Image
Into the plaster box! This is a top-down photo, where the tree has been screwed onto the side of the box by dint of a small hole and bolt. It's important to leave a comfortable margin between the wax and the sides of the box. I generally go for about 15-20mm (about 3/4 inch for you Yanks)

Image
The actual box design. All it is is four sheets of steel, two are 350 x 300mm, and two are 650 x 300mm. The last 50mm of each long end is then folded in a right angle. These sheets then form the four sides of a box, with the folded tabs butting up against the neighbouring sheet enabling them to be clamped together. The clamps were made out of 25 x 6mm flat bar mild steel, with holes drilled and tapped to take four bolts running along the length.
This creates a box that can be adjusted to any size inside the length of the sheets, and if you need a larger box, just cut some longer sheet steel. It has, of course, no bottom. Put a sheet of something underneath (I use sheet steel), and then seal the join all around (I'm using masking tape here, which is enough to do the job).

Image
The plaster goes in. It would have been nice to take a few photos of pouring the plaster, but I'm working on my own here and frankly it's either pour plaster or take photos, and the plaster's setting fast. Suffice to say it's a fraught operation as plaster is heavy and if you pour the weight of it on your wax tree you will likely knock something loose, so you have to be careful (and you didn't skimp on the wax drips when attaching the waxes to the stalk, did you? This is when it comes back to bite you). However, the plaster is also setting very soon, so you have to be fast. Careful and fast; a wonderful combination.
To help the plaster get into all the spaces, and to try to displace bubbles, I've also stabbed my fingers nto the mix and agitated them around a bit. Tapping the outside walls of the box to try and create ripples also sometimes works.
Another point. The plaster is heavy, and any decent height of it (15cm or so) will bow the sides of the box if made out of the thin material I have. Brace them with something.

The plaster mix here is 500ml plaster to 500ml grog* to 500ml water per litre capacity of the box. This makes a firm mix that I'm experienting with, and I may add a little more water on later jobs. The firmer the mix, the harder it is to pour and get into intricate spaces but the better the plaster quality you get for firing.
* Grog is an aggregate added to improve the thermal shock and crack resistance of plaster and ceramic. It can be made out of many different things, eg firebrick, fired ceramic, or in this case old fired plaster (which I seem to have a lot of lying about, for some reason :) ) I don't actually know that it iproves crack resisitance of the plaster, but I'm pretty damn sure it means I don't have to use as much fresh plaster with every cast.

Image
After the plaster's hardened, the aluminium stalk is removed (come on, you didn't actually think it was staying in there did you? How would I pour the metal in?) This set up is just a bolt screwed into the hole in the base of the stalk through a brace, and a nut screwed down the bolt pushing against the brace therefore pulling the bolt (and stalk) up. Note carefully the extremely shoddy welding on show. If I ever offer to do some welding for you, RUN!!!

Image
With the stalk gone, the pourer is clear, including a nice funnel. The three dark splotches near the rim are the three whistlers to let air out. While they are around where I'll be pouring metal, near the rim like that they're not a problem (and it's just so bloody convenient, being able to attach it all together in one portable lump)

Around this point, I notice I'm not wearing my wedding ring, which I always wear despite that over the last couple of years it's become a bit loose. It must have slipped off somewhere. When do I last remember it being on my finger? I don't. What have I done today where it could possibly have slipped off without me noticing? Sudden recollection of me stabbing my fingers in and out of thick setting plaster. Oh shit...

Image
The next step is to take the wax out, preferably recovering as much as possible of it for re-use.
It would be possible to do this in an oven, put the plaster in upside down and melt it out, except for a few problems. Firstly, it seems that if the plaster is allowed to dry prior to the firing process, it worsens cracking during the firing; secondly, the wax tends to soak into the plaster instead of dripping out the holes; finally, melting wax out of a heavy block of plaster is a long operation, and if left unattended in an oven the wax may reach smoking temperature, and possibly even catch fire. For these reasons, my preferred method is to immerse the plaster in water and bring the water to boil. It keeps the plaster moist (which also prevents the wax from soaking in), the temperature wont exceed 100C (so no risk of burning the wax, or the building), you can leave it and a large enough body of water will hold its heat long enough to do the job before it gets cold, and the wax collects on top of the water for easy removal. What you see here is an old-style garbage bin. If you look closely, you may see the plaster mould under the murky surface.

Image
In a perfect world, I'd have a little gas barbeque burner set up to heat the bin, running off the TAFE gas, to do the heating, but this isn't and I don't. Instaed, I heat up brass ingots in the furnace and quench them in the water. Nine quenches or so does the trick. I have to keep and eye on the ingots, since I am, after all, heating them in a furnace built to melt the things. The metal can get soft and mushy if you leave it to red-orange.
I did at first use iron ingots, which have a higher melting point, but after a while of heating and quenching they shattered. :|

The red end is the end that rises proud of the crucible in the direct flame, and therefore is hotter than the rest of the ingot.
Image

Image

Image

Image
The plaster is left in the water until the next class day (in two days time). That night, as I'm straightening out the sheets in the bed something small, round and golden flies out and lands on the floor. Thank Christ for that.
The next work day, the wax is in a hard layer on the surface. Weighing the wax, it comes to close to 100g. Not too bad.

I might just post this now, before something unfortunate happens. :)
“I am the King of Rome, and above grammar”
Sigismund, Holy Roman Emperor
User avatar
Korto
Jedi Master
Posts: 1196
Joined: 2007-12-19 07:31am
Location: Newcastle, Aus

Re: The Genesis of a Lord of Change

Post by Korto »

Continuing on.

Image
The plaster now goes into the kiln for firing. This is an electric pottery kiln (for electric pottery, obviously :) ) and the plaster is inside a steel box, for ease of transport later.
The only direction I've ever seen or this had the plaster being heated at 200C for an hour, 400C for an hour, and then 732C for four hours, before cooling it down to 350C for casting. I then had to work out how that applies to a pottery kiln where you set a target temperature, and when the kiln reaches that temperature, it switches off. I don't have the time to babysit the damn thing. So what I do is I set the kiln at 850C at the slowest possible rate of increase, and walk away.

Things I used to do, and found either unnecessary, or bad:
1) I would fill the rest of the box with sand before putting it in the kiln, in the thought that this would act as a temperature buffer, and possibly counteract cracking (by giving physical support). The only effect it had upon cracking was it prevented the plaster from being fired correctly by providing too large a body to heat, and possibly acting as insulation. It also made the box, which is a one foot cube using 8 gauge steel and therefore already heavy enough before a large lump of plaster was put in it, almost unmanageable (particularly combined with (2) below). I now, as you can see, put it in empty.
2) I would take the plaster out while it was still over 300C for casting, feeling that it was necessary to get good flow through all the thin bits. One day, I decided to try taking it out and pouring it cold. Poured just fine, and so I'm no longer trying to handle something at a temperature where welding gloves give you less than five seconds protection

Image
The fired plaster, with cracking from the firing process. This firing was a bit of an experiment, as before I was firing at 900C, and the cracking was noticeably worse. Next time I might try 800C and see what I get. I do know, however, that 700C is too low, asn I tried it once (by accident). You don't get any cracking, mainly because the plaster isn't fired properly. But don't worry, the water comes out when you pour the molten metal in. Very energetically, and spitting the molten metal back out the damn pourer into the air. Doesn't make for a good result.

Image
You can see here the steel box peeling after being exposed to kiln temperatures. A box made of 8 gauge steel seems to last me about a year before needing replacement. Fortunately I can get the sheeties next door t make me a new one. :)

Image
The poure hole is covered before sand is poured in to fill the rest of the box. There's two reasons for the sand, and they're both that the plaster is quite fragile now. Firstly, it holds it firm and safe while the box and plaster is being moved, and secondly it braces the plaster while the metal is being poured (I have had a plaster burst a side. It didn't have sand support because it was too large to fit in the box).

Image
Cool picture of the furnace.

Image

Image
With the metal (in this case bronze, 8 parts copper to 1 part tin) molten and up to temperature, the dross is scraped off the surface (very little in this case. That particular alloy has a cleanly nature, and came from a clean source)

Image
And finally the metal is poured.

Image
The mould is filled to the brim of the pourer spout and then left to cool. Given the plaster and insulating sand, this will take a fair while. Try not to be too impatient, breaking the plaster apart too early can result in burns, and more importantly possibly damage or even ruin your casting.

Image

Image
Excess metal is poured off. Remember to always put in more metal than you need; not only does it help the metal keep its heat for longer, but there are no prizes for correctly guessing the exact amount you need, and the penalty for under-guessing is final and without appeal.

Image
That would seem to be long enough. Time to start chipping it out and see what I got.

Image

Image

Image

Image
Well, this looks hopeful. Here, however, we're seeing the problem with putting as many waxes as you can on one stalk. It's created a chaotic mess which offers few obvious paths to cut the different pieces loose.

A note on power tools for cutting these things loose. DO NOT USE YOUR ANGLE GRINDER! Your angle grinder hates you. It's always hated you, it's secretly been plotting all this time to gt you, and it sees this as its chance. Put it AWAY!
What about the other tools, you ask?
They all hate you, too (the angle grinder got to them), and they're buring for the chance for your attention to wander so they can dstroy in a moment what you worked so hard on for so long. So what to do? Choose low-powered, slow tools; hack saws, files, the dremel; they all still hate you but they're unable to do anywhere near the same amount of damage in the same short time as a bloody angle grinder.

Image
Finally, after days of work I've managed to cut the Lord of Change clear without damaging any of the other pieces. I've also decided next time to vastly simplify the stalk by only putting figures on two opposite sides, not all around. This should give me easy access through the two clear sides. It just took too long and too much worry to make the crowded stalk worth it.

Image

Image
Finally, I'm left with this. Still a bit of plaster here and there in "hard to reach" places. I may try soaking the whole thing in vinegar for a few weeks to see if I can dissolve it. Also, air bubbles in the plaster have been a problem again (they form bronze lumps on the casting). I recently heard that spraying the wax with diluted detergent can prevent that. Sounds reasonable and worth a try. The three-part-staff hasn't worked in my opinion (or for that matter, in the opinion of my wife and an itenerant friend), but I'm impressed with how the figure is able to stand on its own two feet without needing the tail section to hold it up (not really visible in the picture is that it isn't resting on the tail section.

All in all, I like him. (The pictures don't really do him justice)
“I am the King of Rome, and above grammar”
Sigismund, Holy Roman Emperor
User avatar
Kuja
The Dark Messenger
Posts: 19322
Joined: 2002-07-11 12:05am
Location: AZ

Re: The Genesis of a Lord of Change

Post by Kuja »

I have to give you some major props for all this, Korto. Going out and smelting your own Change lord is pretty fucking awesome, and that's without the fact that you got so damn creative with it. I love the design with the eyestalks and the hands and feet, and it's too bad the staff didn't really work out as well as you'd hoped. You might be able to salvage it though, if you work in a bit of plastic or resin - or even glue - to make it look organic and flowing.

I can't wait to see this thing painted. Major, major kudos to you, dude. That is some fucking epic work.
Image
JADAFETWA
User avatar
Thanas
Magister
Magister
Posts: 30779
Joined: 2004-06-26 07:49pm

Re: The Genesis of a Lord of Change

Post by Thanas »

Indeed.
Whoever says "education does not matter" can try ignorance
------------
A decision must be made in the life of every nation at the very moment when the grasp of the enemy is at its throat. Then, it seems that the only way to survive is to use the means of the enemy, to rest survival upon what is expedient, to look the other way. Well, the answer to that is 'survival as what'? A country isn't a rock. It's not an extension of one's self. It's what it stands for. It's what it stands for when standing for something is the most difficult! - Chief Judge Haywood
------------
My LPs
User avatar
Fingolfin_Noldor
Emperor's Hand
Posts: 11834
Joined: 2006-05-15 10:36am
Location: At the Helm of the HAB Star Dreadnaught Star Fist

Re: The Genesis of a Lord of Change

Post by Fingolfin_Noldor »

If you paint it, it will look better. :)
Image
STGOD: Byzantine Empire
Your spirit, diseased as it is, refuses to allow you to give up, no matter what threats you face... and whatever wreckage you leave behind you.
Kreia
User avatar
Korto
Jedi Master
Posts: 1196
Joined: 2007-12-19 07:31am
Location: Newcastle, Aus

Re: The Genesis of a Lord of Change

Post by Korto »

Yay! Feedback!

Yeah, while I'm a little sorry the staff didn't turn out as I wanted, I'm not at all sorry I tried. I'll try it again one day, too, and do a better job of it.
I had also never considered using resin to fix problems on the finished bronze (maybe because, done properly, there shouldn't be any problems). It's a good idea.

Right now, I've got the lord of change, and a bloodthirster I made for the wife soaking in vinegar to see if it'll save me the trouble of cleaning out the last of the plaster, and I've finished the wax of an emissary of Slanesh. No-one I know has a Slanesh army, or plans to, but I just wanted a Slanesh figure done properly, goddammit. It's come out brilliant, and is definetely not G rated. With the holidays nearly here, it'll be weeks until the thing's cast, but imagine she-male meets tentacle fetish meets bestiality, and it's calling for you...

I've also got to do a couple of chariots, and horrors, flamers, screamers, bloodletters, and khorne hounds. Busy, busy, busy.

Agree on the painting. Ye gods. Painting. Haven't done any of that for years. Wonder if my paints are still OK?
“I am the King of Rome, and above grammar”
Sigismund, Holy Roman Emperor
User avatar
Akhlut
Sith Devotee
Posts: 2660
Joined: 2005-09-06 02:23pm
Location: The Burger King Bathroom

Re: The Genesis of a Lord of Change

Post by Akhlut »

Did you manage to recover your wedding ring?
SDNet: Unbelievable levels of pedantry that you can't find anywhere else on the Internet!
User avatar
Korto
Jedi Master
Posts: 1196
Joined: 2007-12-19 07:31am
Location: Newcastle, Aus

Re: The Genesis of a Lord of Change

Post by Korto »

Yeah, found it that nght. You'll find at the end of the first post...
That night, as I'm straightening out the sheets in the bed something small, round and golden flies out and lands on the floor. Thank Christ for that.

Obviously the damn thing had slipped off my finger while I was asleep.
“I am the King of Rome, and above grammar”
Sigismund, Holy Roman Emperor
User avatar
Korto
Jedi Master
Posts: 1196
Joined: 2007-12-19 07:31am
Location: Newcastle, Aus

Re: The Genesis of a Lord of Change

Post by Korto »

Final push is on to get all the Tzeentch stuff cast before TAFE finishes for the year (in three weeks now), so I've got a mounting pile of metal figures, with flash, bubbles, plaster, air-lines, and all the other garbage that I've got to clean off. Give me something to do over the holidays.

This girl (?) however, not Tzeentch, I got the urge to make because I wanted to see a Slaneshi greater daemon done properly for once, and decided to clean her up today (well, the first clean. It'll need another. and then possibly another).
I guarantee you GW will never make a figure like this.

Image Image
Spoiler
aaarrrgh! Image
Figure notes
The left-arm tentacles caused a bit of trouble. On the side view, you can see there's only two long ones (not couning the one curled around the butt). There's supposed to be six, but the other four froze short. Possible solutions for this are to use a centrifuge (impossible), heat the mould to high temperature first so it wont chill off the metal (impractical), or next time make fewer but thicker tentacles which will hold their heat better.

In fact, if you look closely (side photo) at the long tentacle just below its* hand, you'll see a line across its width. That's actually a clean break, breaking the tentacle in two at that point. What's caused it is metal shrinkage; as the tentacle shrank it pulled against the plaster mould and it couldn't take the strain. I've left the small section of air-line attached to the tip to hold it all in place against a future brazing job (carried out by someone other than me. I need a lot more practise before I attempt something that fine. Ironically, it was likely the air-line that caused it, locking it in place, else it may have been able to pull back down the line a little.
But no air-line = trapped air =/= successfully cast tentacle.

Methodology Notes
1) I'm now setting the kiln at 800C, and that's working pretty well
2) I'm now using chilled (fridge) water when mixing the plaster, and that's working very well (other then having to plunge my hands in icy water). I recommend anyone mixing plaster and wanting as long as possible before the stuff sets to do this.
3) ALWAYS remember when casting hollows to think about whether air will be trapped within the hollow and therefore the plaster will not get in. No plaster, no hollow, just a big mass of metal.

I'll add more to this as stuff gets cleaned up.

* Exactly what gender to call this thing? He? She? Or, (and with all respect to the transgenders on this site who I have nothing but respect for) "It". :lol:
“I am the King of Rome, and above grammar”
Sigismund, Holy Roman Emperor
Post Reply